Polyphenylene oxide mod. flame-retardant (PPO V0)



We use this material in the following process(es):


  • Thermoplastic structure foaming (TSF).
    Multi functional parts and housings up to 16 kg


General properties
Material number 2251
Density ISO 1183 1,05 g/cm³
Transparency op
Condition of the test specimen

Mechanical properties
Stress at yield ISO 527 45 MPa
Tensile strength ISO 527 40 MPa
Elongation at break ISO 527 40 %
Tensile modulus ISO 527 2400 MPa
Tensile creep modulus (0,5% 1000h) ISO 899-1 MPa
Flexural strength ISO 178 70 MPa
Flexural fatigue strength (107 cycles) ASTM D671 MPa
Ball pressure hardness ISO 2039-1 MPa
Standard for ball pressure hardness
Hardness Shore (A/D) or Rockwell (R/L/M) ISO 868, ISO 2039-2 -
Izod impact strength 23 °C ISO 180/1C KJ/m²
Izod impact strength -30 °C ISO 180/1C KJ/m²
Izod notched impact strength 23 °C ISO 180/1A 15 KJ/m²
Izod notched impact strength -30 °C ISO 180/1A 5 KJ/m²
Charpy impact strength 23 °C ISO 179/1eU KJ/m²
Charpy impact strength -30 °C ISO 179/1eU KJ/m²
Charpy notched impact strength 23 °C ISO 179/1eA KJ/m²
Charpy notched impact strength -30 °C ISO 179/1eA KJ/m²
Izod notched impact strength 23 °C ISO 180/4A J/m
Izod notched impact strength -40 °C ISO 180/4A J/m
Friction against steel without lubrication -
Abrasion relative to pressure (µm/km)/MPa

Electrical properties
Dielectric constant 50 Hz IEC 60250 2,3 -
Dielectric constant 1 MHz IEC 60250 2,2 -
Dissipation factor 50 Hz IEC 60250 47 10-4
Dissipation factor 1 MHz IEC 60250 39 10-4
Dielectric strength IEC 60243-1 kV/mm
Thickness for electric strength mm
Volume resistivity IEC 60093 Ω · m
Surface resistivity IEC 60093 1E17
Comparative tracking index IEC 60112 -
Comparative tracking index CTI M IEC 60112 -

Thermal properties
Thermal conductance DIN 52 612 0,24 W/K m
Specific heat IEC 1006 1,26 J/g K
Linear thermal expansion along|cross to direction of flow ISO 11359 70-80 10-6/K
Melting point ISO 11357 105 27) °C
Heat distortion temperature A ISO 75 HDT/A (1,8 MPa) 90 °C
Heat distortion temperature B ISO 75 HDT/B (0,45 MPa) 95 °C
Vicat softening point A ISO 306 VST/A/50 (10 N) °C
Vicat softening point B ISO 306 VST/B/50 (50 N) 100 °C
Short time use temperature 100 °C
Continuous use temperature 90 °C
Minimal use temperature -50 °C

Chemical properties
mineral oils o
Aliphatic hydrocarbons o
Aromatic hydrocarbons
Petrol
Weak mineral acids +
Strong mineral acids o
Weak organic acids +
Strong organic acids o
Oxidising acids o
Weak alkalis +
Strong alkalis +
Trichlorethylene
Perchlorethylene
Acetone
Alcohol +
Hot water (hydrolysis resistance) +
UV-light and weathering o

Other properties
Humidity absorption at 23°C/50% ISO 62 <0,1 %
Water absorption ISO 62 0,2 %
Flammability UL 94 IEC 60695-11-10 V-0 / 5VA -
Thickness for UL 94 4,0 mm
Limiting oxygen index ISO 4589 29 %
Raw material Noryl FN150 (Sabic)

Remarks


27): Softening point according to Vicat VST/B/120
na: not applicable
+: resistant
o: partly resistant
-: not resistant

The figures in this datasheet are guide values. The values are affected by processing conditions, modifications, additives and environmental conditions and they do not release you from the obligation to check the validity and to undertake tests on your own. The information given is based on our state of knowledge. The material data is not to be construed as guaranteeing specific properties and the data can not be used to deduce the suitability for a particular application.

It remains the responsibility of the user of our products not to infringe patent rights and to comply with existing laws and regulations.